Technical Specifications
Units
CONDITIONS
Tensile Modulus
MPa
DIN EN ISO 527
3800 +/- 150
Tensile Strength
MPa
DIN EN ISO 527
48 +/- 3
Elongation at Break
%
DIN EN ISO 527
3.5 +/- 5
Flexural Modulus
N/mm²
DIN EN ISO 178
3600 +/- 150
Charpy – Impact strength
MPa
DIN EN ISO 179
29 +/- 2
Charpy – Notched Impact Strength
MPa
DIN EN ISO 179
4.6 +/- 0.3
Izod – Impact Strength
J/m²
DIN EN ISO 180
N/A
Izod – Notched Impact Strength
J/m²
DIN EN ISO 180
N/A
Ball Indentation Hardness
DIN EN ISO 2039
N/A
Shore Hardness (D)
DIN 53505
76 +/- 2
Heat Deflection t°
°C
ASTM D648 (1.82 MPa)
130
Vicat Softening Temperature B/50
°C
DIN EN ISO 306
169
Vicat Softening Temperature A/50
°C
DIN EN ISO 306
N/A