Technical Specifications
Units
CONDITIONS
Tensile Modulus
MPa
DIN EN ISO 527
1650 +/- 150
Tensile Strength
MPa
DIN EN ISO 527
48 +/- 3
Elongation at Break
%
DIN EN ISO 527
20 +/- 5
Flexural Modulus
N/mm²
DIN EN ISO 178
1500 +/- 130
Charpy – Impact strength
MPa
DIN EN ISO 179
53 +/- 3.8
Charpy – Notched Impact Strength
MPa
DIN EN ISO 179
4.8 +/- 0.3
Izod – Impact Strength
J/m²
DIN EN ISO 180
32.8 +/- 3.4
Izod – Notched Impact Strength
J/m²
DIN EN ISO 180
4.4 +/- 0.4
Ball Indentation Hardness
DIN EN ISO 2039
77.6 +/- 2
Shore Hardness (D)
DIN 53505
75 +/- 2
Heat Deflection t°
°C
ASTM D648 (1.82 MPa)
86
Vicat Softening Temperature B/50
°C
DIN EN ISO 306
163
Vicat Softening Temperature A/50
°C
DIN EN ISO 306
181