Caractéristiques techniques
Alloy Family
AlSi10Mg
Unités
Norme
RANGE (AFTER HEAT TREATMENT)
Density
g/cm³
> 2.59
Résistance à la traction
MPa
DIN EN ISO 6892-1:2009 B
250 - 330
Elongation at Break
%
DIN EN ISO 6892-1:2009 B
1.0 - 4.0
E- modulus
GPa
DIN EN ISO 6892-1:2009 B
50 - 70
Yield Strength
MPa
DIN EN ISO 6892-1:2009 B
180 - 220
Hardness
HV
ISO 6597-1: 03-2006 HV0,2
> 80
Relative Density
%
> 97.0
Roughness Ra
µm
ISO 4287 / AITM 1-0070
< 16
Roughness Rz
µm
ISO 4287 / AITM 1-0070
< 70
We recommend to avoid the use of this material for static and dynamic loads.
Actual values may vary with build conditions and can't not be guaranteed.
Strong tensions, due to part geometry, may cause distortion in the part which may lead to greater deviation.